Contractor Grade Sliding Wear Compound


Code: BX1
Name: Contractor Grade Sliding Wear Compound

An advanced contractor grade ceramic composite for the repair and  protection of all metal surfaces subjected to severe erosion, corrosion,  and chemical attack.  ARC BX1 is formulated with a high concentration of ceramic beads and  fine ceramic particles for extremely abrasive environments where metal  loss is often repaired by more conventional and costly weld overlay. It is normally applied at a thickness of 6 mm (1/4 inch)  or more.

Technical Data

  • Dry Temperature Dry (Min/Max)                                           -20 F (-29C) to 400 F (205 C) 
  • Wet Temperature (Min/Max)                                                 -20 F (-29C) to 205 F (95 C) 
  • Compressive Strength - kg/cm2 - Mpa (psi)                      590 - 58 (8,400) 
  • Flexural Strength - kg/cm2 - Mpa (psi)                                340 - 33 (4,800) 
  • Tensile Strength - kg/cm2/Mpa (psi)                                    220 - 22 (3,100) 
  • Tensile Adhesion - kg/cm2 - Mpa (psi)                                Greater than 123 - 12 (1,750) 
  • Impact Resistance - nt m (in. lbs.)                                        6,6 (58) 
  • Water Vapor Permeability
  • (meteric perm-cm - Perms)  
  • Salt Fog  
  • Shore D Hardness                                                                    85