ARC BX2 is an advanced contractor grade ceramic reinforced composite for  the repair and protection of all metal surfaces subjected to severe erosion,  corrosion, and chemical attack. ARC BX2 is formulated with a high concentration of small ceramic beads and  particles for extremely abrasive environments where metal loss is often  repaired by more conventional and costly weld overlay. ARC BX2 is a long lasting wearing  surface and is chosen over ARC BX1 where a thinner, more easily applied  composite is required.

TECHNICAL DATA

• Dry Temperature Dry (Min/Max)                                            -20 F (-29C) to 400 F (205 C)
• Wet Temperature (Min/Max)                                                  -20 F (-29C) to 205 F (95 C)
• Compressive Strength - kg/cm2 - Mpa (psi)                      900 - 88 (12,800)
• Flexural Strength - kg/cm2 - Mpa (psi)                                650 -64 (9,250)
• Tensile Strength - kg/cm2/Mpa (psi)                                    320 - 31 (4,550)
• Tensile Adhesion - kg/cm2 - Mpa (psi)                                Greater than 123 - 12 (1,750)
• Impact Resistance - nt m (in. lbs.)                                        5,8 (51)
• Water Vapor Permeability (meteric perm-cm - Perms) 
• Salt Fog 
• Shore D Hardness                                                                    90